MgO-C Bricks for BOF
MgO-C Bricks for EAF
MgO-C Bricks for Ladle
Al2O3-MgO-C Bricks for Ladle
Alumina-SiC-C for Torpedo
MgO-C Bricks for RH Furnace
Castables for Blast Furnace Trough
Castables
Repairing material for BOF
Ramming Mix for EAF Bottom
Gunning Mix for Converter and Ladle
Raw Material
Slide Gate Plate
Lower/Upper Nozzle Brick
 

This material uses fused magnesia or sintered magnesia as the main raw material and after modifid pitch and special additives are added,it has the following characteristcs than other conventional converter pitch temperature,shorter sintering time,longer service life and less pollution .
It is mainly used for repairing converter working face,also for tapping side,tapping hole and bottom.

Material BOF repairing material
Brand JHR-RM01 JHR-RM02
phy chemproty Standard Standard
Chemical Composition(%) MgO 79 78
CaO 2 2
F.c 7 5
Bulk density g/cm3 110*12h 2.5 2.5
felt strength of high temp Mpa 1000 12 9
Modulus of Rupture(Mpa) 1400 38 20
Application BOF encase side BOF tapping side & bottom of BOF
Above data are our standard specification, And there is a series products for a single grade bricks to meet the consumers' different demands.